Raise3D Premium ABS 3D Printing Filament

High-quality 1.75 mm ABS 3D printing filament featuring high mechanical strength, impact resistance, and heat resistance up to 90 °C. Integrated RFID tag allows compatible Raise3D printers to automatically recognize the filament and verify print parameters.

In stock

Price

from34,99 €

Skersmuo

1.75 mm

Spalva

Black
Grey
White

Clear

Need a larger quantity? Contact us for custom pricing on larger quantity orders.

About Raise3D Premium ABS

Raise3D Premium ABS is a professional ABS (acrylonitrile butadiene styrene) 3D printing filament designed for producing strong, durable, and functional parts. ABS is one of the most widely used industrial thermoplastics, featuring excellent mechanical properties, impact resistance, and good thermal resistance up to 90 °C.

This material is ideal for prototyping, functional testing, part assembly, and manufacturing process aids. ABS printed parts can be used both without post-processing and with various surface finishing treatments.

Integrated RFID tag allows compatible Raise3D Pro3 HS series 3D printers to automatically recognize the filament type and verify recommended print parameters. The filament can also be used with other compatible Raise3D printers.

Property	Test Method	Typical Value
Density (g/cm³ at 23 °C)	ISO 1183, GB/T 1033	1.12
Glass Transition Temperature (°C)	DSC, 10 °C/min	101 °C
Vicat Softening Temperature (°C)	ISO 306, GB/T 1633	104 °C
Melt Flow Index (g/10 min)	220 °C, 2.16 kg	9–14 g/10 min
Decomposition Temperature (°C)	TGA, 20 °C/min	> 380 °C
Heat Deflection Temperature (°C)	ISO 75, 0.45 MPa	98 °C
Heat Deflection Temperature (°C)	ISO 75, 1.8 MPa	100 °C
Long-Term Service Temperature (°C)	–	–20 to 90 °C
Odor	–	Nearly odorless
Solubility	–	Insoluble in water
Flammability Rating	UL94, 1.5 mm	HB

Note: Tests performed using 3D printed specimen with 100% infill.

Property	Test Method	Typical Value
Young's Modulus (MPa, X–Y)	ISO 527, GB/T 1040	2174 ± 285 MPa
Tensile Strength (MPa, X–Y)	ISO 527, GB/T 1040	33 ± 1 MPa
Elongation at Break (%, X–Y)	ISO 527, GB/T 1040	2.7 ± 0.4 %
Flexural Modulus (MPa)	ISO 178, GB/T 9341	2850 ± 300 MPa
Flexural Strength (MPa)	ISO 178, GB/T 9341	73 ± 1 MPa
Charpy Impact Strength (kJ/m²)	ISO 179, GB/T 1043	12.6 ± 1.1 kJ/m²

Note:

All specimens were printed under the following conditions:

Nozzle Temperature: 255 °C
Print Speed: 60 mm/s
Build Platform Temperature: 100 °C
Infill: 100%

All tests performed using 3D printed specimens with 100% infill.

Parameter	Recommended Setting
Nozzle Temperature (°C)	245–265 °C
Build Surface Material	BuildTak®
Build Surface Preparation	–
Build Platform Temperature (°C)	90–105 °C
Cooling Fan	Off
Print Speed (mm/s)	30–50 mm/s
Raft Separation Distance (mm)	0.20 mm
Retraction Distance (mm)	1 mm
Retraction Speed (mm/s)	20 mm/s
Recommended Ambient Temperature (°C)	20–50 °C
Critical Overhang Angle (°)	50°

Note: Recommended settings provided using 0.4 mm diameter nozzle and ideaMaker software. Print settings may vary when using different diameter nozzles.

Technical Data Sheet
Safety Data Sheet

Key Benefits of Raise3D Premium ABS Filament

Balanced Mechanical Properties
Easy Post-Processing
Chemical Resistance

Application Areas

Functional Prototyping

Tools and Fixtures

Prototypes and Concept Models

Frequently Asked Questions

Raise3D Premium ABS is a professional ABS-based 3D printing filament designed for producing strong, durable, and functional parts. It features excellent mechanical properties, heat resistance, and is suitable for prototyping and production applications.

The filament is optimized for Raise3D 3D printers. It can also be used with other compatible FFF/FDM type 3D printers.

ABS is a widely used industrial thermoplastic characterized by high strength, impact resistance, good heat resistance, and the ability to perform post-processing.

Yes. ABS parts can be sanded, post-processed, and otherwise modified after printing, which is why this material is often used for professional prototypes.

View all FAQ